CHAPTER 4 - AIRCRAFT WELDING
Question | Answer |
---|---|
NAME THE THREE PRINCIPLE TYPES OF WELDING. | GAS WELDING, ELECTRIC ARC WELDING, AND ELECTRIC RESISTANCE WELDING. |
WHAT ARE SOME ADVANTAGES OF GAS SHIELDED ARC WELDING? | THE WELD IS STRONGER, MORE DUCTILE, AND MORE CORROSION RESISTANT. |
WHICH METHOD OF WELDING IS LESS LIKELY TO CAUSE BUCKLING OR WARPING OF THIN METAL SHEETS? | ELECTRIC ARC (OR TIG) WELDING. |
WHAT IS THE PURPOSE OF SHIELDING AN ARC WELD WITH AN INERT GAS? | THE GAS PREVENTS ATMOSPHERIC OXYGEN AND/OR NITROGEN FROM CONTAMINATING THE WELD. |
WHAT IS A COMMON METHOD OF CONTROLLING EXPANSION WHEN WELDING A JOINT? | PLACE TACK WELDS ALONG THE LENGTH OF THE JOINT. |
WHAT IS THE EFFECT OF INADEQUATE PENETRATION ON A WELD? | THE WELD WILL BE WEAK. |
WHAT IS THE PURPOSE OF THE FLUX USED WITH BRAZING AND SILVER SOLDERING. | THE FLUX CLEANS THE BASE METAL BY REMOVING ANY OXIDE FILM. |
WHAT TYPE OF FLAME IS USED WHEN TORCH BRAZING OR SILVER SOLDERING? | A NEUTRAL FLAME. |
WHAT MUST BE DONE TO A SOLDERING IRON TIP TO INCREASE THE AMOUNT OF HEAT TRANSFERRED FROM THE TIP TO THE WORK? | THE TIP MUST BE CLEAN OF ALL CONTAMINATES AND PROPERLY TINNED |
WHAT IS THE PERFERRED METHOD FOR WELDING ALUMINIUM? | TUNGSTEN INERT GAS (TIG) WELDING. |
WHAT IS THE PERFERRED METHOD FOR WELDING MAGNESUM? | TUNGSTEN INERT GAS (TIG) WELDING. |
WHAT PRECAUTIONS MUST BE OBSERVED IN ORDER TO WELD TITANIUM? | ALL TRACES OF OXYGEN AND NITROGEN MUST BE KEPT AWAY FROM THE WELD AREA. |
DESCRIBE ONE TYPE OF REPAIR THAT COULD BE MADE TO A DENTED STEEL TUBE CLUSTER JOINT. | A FORMED STEEL PATCH PLATE COULD BE WELDED OVER THE DAMAGED AREA. |
HOW CAN A SOFT FLAME BE OBTAINED WITHOUT REDUCING THE HEAT OUTPUT OF THE TORCH? | USE A LARGER TIP AND ADJUST THE GAS PRESSURE ACCORDINGLY. |
WHAT FACTORS DETERMINE THE AMOUNT OF HEAT DELIVERED BY A GAS WELDING TORCH? | THE SIZE OF THE TORCH TIP AND THE GAS PRESSURE. |
WHEN AN OXYACETYLENE TORCH IS EXTINGUISHED, WHICH VALVE IS TURNED OFF FIRST? | TURN OFF THE ACETYLENE GAS VALVE FIRST. |
WHEN A GAS WELDING PROJECT IS COMPLETED , WHAT SAFETY PRECAUTIONS SHOULD BE ACCOMPLISHED? | ALL THE VALVES ARE TURNED OFF AND THE GAS PRESSURES ARE RELIEVED. |
WHAT SHOULD BE DONE TO A HEAT-TREATED ALUMINUM PART AFTER WELDED REPAIRS ARE COMPLETED? | THE PART MUST BE RE-HEAT TREATED. |
WELDING MAGNESIUM CAN CREATE A SERIOUS SAFETY HAZARD. WHAT IS THE NATURE OF THIS HAZARD? | MAGNESIUM BURNS WITH A VERY HOT FLAME THAT IS VERY HARD TO EXTINGUISH. |
WHAT TECHNIQUE MIGHT BE USED TO ENABLE A TIGHT-FITTING INNER SLEEVE TO BE INSERTED INTO A TUBULAR REPAIR? | THE INNER TUBE COULD BE CHILLED WITH DRY ICE OR IN A FREEZER WHILE THE OUTER TUBE COULD BE HEATED SLIGHTLY WITH A TORCH. |